What are the factors that affect the service life of steel shot?

　　Any product will be lost due to various reasons during use. In order to prevent excessive consumption of steel shots during use, it is necessary to understand the factors that affect the service life of steel shots, so as to effectively prevent some problems. Here the manufacturer introduces two influencing factors.

　　1. The hardness of the steel shot determines the service life of the steel shot

　　The hardness of the steel shot is directly proportional to the finishing speed. The higher the hardness, the faster the finishing speed. On the contrary, the greater the consumption of the steel shot, the shorter the service life. The production process of the steel shot determines that the size of the steel shot is not uniform. The larger the diameter, the higher the efficiency of finishing the rough surface, but the wear of the steel shot is also greater.

　　The relationship between steel shot hardness and rebound

　　2. The steel shot that meets the density can have stable quality

　　The density of the steel shot is also an important factor in determining the service life of the steel shot. Only a steel shot with a sufficient density can show stable quality and reduce breakage and wear during the cleaning process.

　　Through the above introduction, we will find that the hardness of the steel shot is directly proportional to the finishing speed, and inversely proportional to the service life. The moderate hardness has excellent resilience, and every corner can be fully cleaned during blasting to reduce the processing time. However, internal defects such as pores, cracks, and shrinkage cavities will directly affect its service life and increase consumption. Therefore, we need to learn more about some factors that affect the service life of steel shot, so that it will be more convenient for our future use.